KT Potassium Talate (KTaO3) Single crystal has a stable cubic structure, and can be used to make laser modulator, digital deflector and semiconductor devices. Due to the absence of phase transition in the temperature range from absolute zero to its melting point (1645K), and the good matching of its cell parameters with yttrium barium copper oxide superconductors, this crystal has the potential to be used as a substrate material for superconducting thin films
Product Description
KT Potassium Talate (KTaO3) Single crystal has a stable cubic structure, and can be used to make laser modulator, digital deflector and semiconductor devices. Due to the absence of phase transition in the temperature range from absolute zero to its melting point (1645K), and the good matching of its cell parameters with yttrium barium copper oxide superconductors, this crystal has the potential to be used as a substrate material for superconducting thin films
Product Parameters
| Molecular formula | KTaO3(KT) |
| Point group | m3m |
| Cell parameters | 0.3984nm |
| Melting point | 1352.2℃ |
| Density | 7.025 g/cm3 |
| Mohs hardness | 6 |
| Growing directions | Czochralski method |
| Refractive index | 2.226@633nm, 2.152@1539nm |
| Thermal expansion coefficient due to heat | 4.027*10-6/K) |
| Specific heat (room temperature JK-1g-1) | 0.378 |
| Transparent band (nm) | 380~4000 |
| Conventional crystal orientation | <100>;<110>;<111> |
| Standard size | 20x20x0.5mm;10x10x0.5mm,5x5x0.5mm, or processed according to customer requirements |
| Polishing | Single throw, double throw, and Ra <1nm |